Mono and Bimetallic bushings and sleeves made by centrifugal casting using bimetallic technology and specific alloys developed in our R&D labs. Cronite alloys provide superior wear resistance due to higher hardness compared to standard alloys.
Bimetallic bushings :
Our alloy HR15CLC is a fully austenitic alloy to reach the best corrosion and wear resistance in the galvanizing pots maintaining a good weldability.
Our alloy HR39E is an intermetallic stainless material able to maintain a hardness 40-50HRC at 460-500°C
You want to contact our team for more information ?